Manufacture of trialkylaluminum compounds and α-alcohols

ABSTRACT

Higher trialkylaluminum compounds may be made by forming α-olefin by oligomerizing ethylene using a transition metal containing catalyst, reacting the α-olefins formed with aluminum and hydrogen to form higher trialkylaluminum compounds. These may optionally be oxidized, as with oxygen, to form higher trialkoxyaluminum compound, which in turn may be hydrolyzed to α-alcohols. Higher trialkylaluminum compounds and α-alcohols are useful as chemical intermediates.

This application claims the benefit of Provisional application Ser. No. 60/340,444, filed Dec. 12, 2001.

FIELD OF THE INVENTION

α-Olefins are manufactured by oligomerizing ethylene using a transition metal containing catalyst, the α-olefins are converted to trialkylaluminum compounds by contacting them with aluminum and hydrogen with heat and pressure. The trialkylaluminum compounds which are formed may be reacted with oxygen to form the corresponding trialkoxyaluminum compounds, which can be hydrolyzed to form α-alcohols.

TECHNICAL BACKGROUND

Higher trialkylaluminum compounds (HTAC), R³¹ ₃Al (I), in which the alkyl groups contain more than 4 carbon atoms, are useful particularly as chemical intermediates for the synthesis of α-alcohols of the formula R³²R³³CHCH₂OH (II) wherein R³² is hydrogen or alkyl and R³³ is alkyl. α-Alcohols containing 10 to 20 carbon atoms are useful as intermediates for the synthesis of detergents and other surfactants. Therefore improved methods of making (I) and/or (II) are commercial interest.

Generally speaking, linear α-alcohols are often made utilizing the following steps, see for Instance B. Elvers, et al., Ed., Ullmann's Encyclopedia of Industrial Chemistry, 5^(th) Ed., Vol. A28, 1996, p. 505-508 and references therein, and J. I. Kroschwitz, et al., Ed, Encyclopedia of Chemical Technology, 4^(th) Ed., Vol. 1, John Wiley & Sons, New York, p. 894-903 and references therein, both of which are hereby included by reference.

(a) Triethylaluminum is produced by contacting under relatively high pressure and temperature a mixture of aluminum, hydrogen, ethylene and triethylaluminum (TEA). “New” TEA is produced in the reactor. The liquid product is removed from the reactor, filtered and some is recycled back to the TEA reactor and some is used in the next step.

(b) The TEA used in the next step is now mixed with more ethylene under high pressure and with heating. The ethylene adds sequentially (oligomerizes) to each of the original ethyl groups in the TEA, forming HTACs.

(c) The product of the previous step is mixed with oxygen (a highly exothermic reaction) to form the corresponding trialkoxyaluminum compounds.

(d) The trialkoxyaluminum compounds are hydrolyzed to form an alpha-alcohol mixture and alumina. This process is effective but requires the use of high temperatures and pressures in two steps, and in these two steps pyrophoric alkylaluminum compounds are present, and so these steps must be done very carefully to protect the plant and workers safety. This adds to the cost of the overall process. Processes which would minimize such steps, and/or require less capital investment, and/or have lower operating costs, would therefore be favored.

U.S. Pat. Nos. 2,787,626, 3,032,574, 3,207,770 and 3,960,912 describe the synthesis of trialkylaluminum compounds from olefins, hydrogen, aluminum, and sometimes other ingredients. The use of olefins made with transition metal containing ethylene oligomerization catalysts is not mentioned.

U.S. Pat. Nos. 6,103,946, 4,689,437, 3,644,564 and 5,382,738, which are all hereby included by reference, describe the use of various transition metal containing catalysts to make olefins or mixtures of olefins by oligomerizing ethylene. No mention is made of making trialkylaluminum compounds or α-alcohols from those trialkylaluminum compounds.

B. Elvers, et al., Ed., Ullmann's Encyclopedia of Industrial Chemistry, 5^(th) Ed., Vol. A28, VCH Verlagsgesellschaft mbH, Weinheim, 1996, p. 505-508 and references therein, and U.S. Pat. No. 5,278,330 describe the overall commercial synthesis processes for making α-alcohols, including the synthesis processes for making HTACs.

SUMMARY OF THE INVENTION

This invention concerns, a process for the manufacture of higher trialkylaluminum compounds, comprising, forming an α-olefin or mixture of α-olefins by oligomerization of ethylene using a transition metal containing oligomerization catalyst system, then contacting said α-olefin or said mixture of α-olefins with aluminum metal, hydrogen and a trialkylaluminum compound at a sufficient temperature and pressure, for a sufficient amount of time, to form a higher trialkylaluminum compound.

This invention also concerns a process for the manufacture of α-alcohols, comprising:

(1) forming an α-olefin or mixture of α-olefins by oligomerization of ethylene using a transition metal containing oligomerization catalyst system;

(2) then contacting said α-olefin or said mixture of α-olefins with aluminum metal, hydrogen and a trialkylaluminum compound at a sufficient temperature and pressure, for a sufficient amount of time, to form a higher trialkylaluminum compound or a mixture thereof;

(3) contacting said higher trialkylaluminum compound or a mixture thereof with oxygen or other suitable oxidizing agent to form a higher trialkoxyaluminum compound or a mixture thereof; and

(4) hydrolyzing said higher trialkoxyaluminum compound or a mixture thereof to form an α-alcohol or a mixture thereof.

DETAILS OF THE INVENTION

Herein certain terms are used, and some of them are defined below:

By a “higher trialkylaluminum compound” (HTAC) is meant a compound of the formula R³¹ ₃Al (I), in which each of R³¹ contains 4 or more carbon atoms, preferably 6 or more carbon atoms, each R¹ is independently R³²R³³CHCH₂—wherein R³² is hydrogen or alkyl, R³³ is alkyl, and each R³¹ contains an even number of carbon atoms. Preferably R³² is hydrogen and/or R³³ is n-alkyl. It is to be understood that the HTAC may contain impurities such as hydrogen bound to aluminum or alkyl groups having less than 4 carbon atoms bound to aluminum, but at least 50 mole percent, more preferably at least 75 mole percent, and especially preferably at least 90 mole percent of the groups bound to aluminum are R³¹—.

By a “higher trialkoxyaluminum compound” (HTAC) is meant a compound of the formula (R³¹O)₃Al (III), in which each of R³¹ contains 4 or more carbon atoms, preferably 6 or more carbon atoms, each R³¹ is independently R³²R³³CHCH₂—wherein R³² is hydrogen or alkyl, R³³ is alkyl, and each R³¹ contains an even number of carbon atoms. Preferably R³² is hydrogen and/or R³³ is n-alkyl. It is to be understood that the higher trialkoxyaluminum compound(s) may contain impurities such as alkoxy groups having less than 4 carbon atoms bound to aluminum, but at least 50 mole percent, more preferably at least 75 mole percent, and especially preferably at least 90 mole percent of the groups bound to aluminum are R³¹O—.

By an α-alcohol is meant a compound of the formula R²R³CHCH₂OH (II), wherein R³² is hydrogen or alkyl, R³³ is alkyl, and (II) contains an even number of carbon atoms. Preferably R³² is hydrogen and/or R³³ is n-alkyl.

By a transition metal containing ethylene oligomerization catalyst is meant a catalyst system which contains an element of Groups 3-12 (IUPAC notation) in the catalyst system, and which is capable of oligomerizing ethylene to an α-olefin. Transition metal containing “inert” supports are not considered part of the catalyst system. By “inert” in this context is meant that the support is believed to function merely as a physical support and does not actually take part chemically in the oligomerization process.

By an “α-olefin” is meant a compound of the formula H₂C═CR³²R³³ (IV) wherein R³² is hydrogen or alkyl, R³³ is alkyl, and (IV) contains an even number of carbon atoms. It is preferred than R³² is hydrogen and/or R³³ is n-alkyl.

Transition metal containing catalysts that oligomerize ethylene to α-olefins may be divided into two classes, those that produce a mixture of α-olefins and those that produce (mostly) a single α-olefin. The former are exemplified by those catalysts found in U.S. Pat. Nos. 6,103,946, 2,787,626, 3,032,574, 3,207,770, 3,644,564, 3,647,915 and 3,647,915, all of which are hereby included by reference. These oligomerizations herein may be run under conditions described in these references and in other references for other such types of catalysts. Typically these catalysts produce a homologous series of α-olefins that differ by two carbon atoms. The amounts of each olefin in the homologous series typically follow a so-called Schulz-Flory distribution, which uses a factor K from the Schulz-Flory theory (see for instance B. Elvers, et al., Ed. Ullmann's Encyclopedia of Industrial Chemistry, Vol. A13, VCH Verlagsgesellschaft mbH, Weinheim, 1989, p. 243-247 and 275-276, which is hereby included by reference). This is defined as:

K=n(C_(n+2) olefin)/n(C_(n) olefin)

wherein n(C_(n) olefin) is the number of moles of olefin containing n carbon atoms, and n(C_(n+2) olefin) is the number of moles of olefin containing n+2 carbon atoms, or in other words the next higher oligomer of C_(n) olefin. From this can be determined the weight (mass) fractions of the various olefins in the resulting oligomeric reaction product mixture. The K factor is preferred to be in the range of about 0.6 to about 0.8

A preferred type of ethylene oligomerization catalyst is described in U.S. Pat. No. 6,103,946 and World Patent Applications 01/58874, 00/42123, 00/76659 and 01/19513, all of which are hereby included by reference, and similar iron tridentate catalysts which result in the formation of α-olefins. These catalysts utilize selected diimines of 2,6-diacylpyridines or 2,6-pyridinedicarboxaldehydes as part of the ethylene oligomerization catalyst system, particularly as iron complexes.

Such a preferred active ethylene oligomerization catalyst comprises an iron complex of a compound of the formula

wherein:

R¹, R² and R³ are each independently hydrogen, hydrocarbyl, substituted hydrocarbyl or an inert functional group, provided that any two of R¹, R² and R³ vicinal to one another taken together may form a ring;

R⁴ and R⁵ are each independently hydrogen, hydrocarbyl, substituted hydrocarbyl or an inert functional group;

R⁶ and R⁷ are each independently a substituted aryl having a first ring atom bound to the imino nitrogen, provided that:

in R⁶, a second ring atom adjacent to said first ring atom is bound to a halogen, a primary carbon group, a secondary carbon group or a tertiary carbon group; and further provided that

in R⁶, when said second ring atom is bound to a halogen or a primary carbon group, none, one or two of the other ring atoms in R⁶ and R⁷ adjacent to said first ring atom are bound to a halogen or a primary carbon group, with the remainder of the ring atoms adjacent to said first ring atom, being bound to a hydrogen atom; or

in R⁶, when said second ring atom is bound to a secondary carbon group, none, one or two of the other ring atoms in R₆ and R⁷ adjacent to said first ring atom are bound to a halogen, a primary carbon group or a secondary carbon group, with the remainder of the ring atoms adjacent to said first ring atom being bound to a hydrogen atom; or

in R⁶, when said second ring atom is bound to a tertiary carbon group, none or one of the other ring atoms in R⁶ and R⁷ adjacent to said first ring atom are bound to a tertiary carbon group, with the remainder of the ring atoms adjacent to said first ring atom being bound to a hydrogen atom.

A “hydrocarbyl group” is a univalent group containing only carbon and hydrogen. As examples of hydrocarbyls may be mentioned unsubstituted alkyls, cycloalkyls and aryls. If not otherwise stated, it is preferred that hydrocarbyl groups (and alkyl groups) herein contain 1 to about 30 carbon atoms.

By “substituted hydrocarbyl” herein is meant a hydrocarbyl group that contains one or more substituent groups which are inert under the process conditions to which the compound containing these groups is subjected (e.g., an inert functional group, see below). The substituent groups also do not substantially detrimentally interfere with the oligomerization process or operation of the oligomerization catalyst system. If not otherwise stated, it is preferred that substituted hydrocarbyl groups herein contain 1 to about 30 carbon atoms. Included in the meaning of “substituted” are rings containing one or more heteroatoms, such as nitrogen, oxygen and/or sulfur. In a substituted hydrocarbyl, all of the hydrogens may be substituted, as in trifluoromethyl.

By “(inert) functional group” herein is meant a group, other than hydrocarbyl or substituted hydrocarbyl, which is inert under the process conditions to which the compound containing the group is subjected. The functional groups also do not substantially deleteriously interfere with any process described herein that the compound in which they are present may take part in. Examples of functional groups include halo (fluoro, chloro, bromo and iodo), and ether such as —OR⁵⁰ wherein R⁵⁰ is hydrocarbyl or substituted hydrocarbyl. In cases in which the functional group may be near a transition metal atom, the functional group alone should not coordinate to the metal atom more strongly than the groups in those compounds that are shown as coordinating to the metal atom, that is they should not displace the desired coordinating group.

By a “primary carbon group” herein is meant a group of the formula —CH₂—, wherein the free valence—is to any other atom, and the bond represented by the solid line is to a ring atom of a substituted aryl to which the primary carbon group is attached. Thus the free valence—may be bonded to a hydrogen atom, a halogen atom, a carbon atom, an oxygen atom, a sulfur atom, etc. In other words, the free valence—may be to hydrogen, hydrocarbyl, substituted hydrocarbyl or a functional group. Examples of primary carbon groups include —CH₃, —CH₂CH(CH₃)₂, —CH₂Cl, —CH₂C₆H₅, —OCH₃ and —CH₂OCH₃.

By a secondary carbon group is meant the group

wherein the bond represented by the solid line is to a ring atom of a substituted aryl to which the secondary carbon group is attached, and both free bonds represented by the dashed lines are to an atom or atoms other than hydrogen. These atoms or groups may be the same or different. In other words the free valences represented by the dashed lines may be hydrocarbyl, substituted hydrocarbyl or inert functional groups. Examples of secondary carbon groups include —CH(CH₃)₂, —CHCl₂, —CH(C₆H₅)₂, cyclohexyl, —CH(CH₃)OCH₃, and —CH═CCH₃.

By a “tertiary carbon group” is meant a group of the formula

wherein the bond represented by the solid line is to a ring atom of a substituted aryl to which the tertiary carbon group is attached, and the three free bonds represented by the dashed lines are to an atom or atoms other than hydrogen. In other words, the bonds represented by the dashed lines are to hydrocarbyl, substituted hydrocarbyl or inert functional groups. Examples of tetiary carbon groups include —C(CH₃)₃, —C(C₆H₅)₃, —CCl₃, —CF₃, —C(CH₃)₂OCH₃, —C≡CH, —C(CH₃)₂CH═CH₂, aryl and substituted aryl such as phenyl and 1-adamantyl.

By “aryl” is meant a monovalent aromatic group in which the free valence is to the carbon atom of an aromatic ring. An aryl may have one or more aromatic rings which may be fused, connected by single bonds or other groups.

By “substituted aryl” is meant a monovalent aromatic group substituted as set forth in the above definition of “substituted hydrocarbyl”. Similar to an aryl, a substituted aryl may have one or more aromatic rings which may be fused, connected by single bonds or other groups; however, when the substituted aryl has a heteroaromatic ring, the free valence in the substituted aryl group can be to a heteroatom (such as nitrogen) of the heteroaromatic ring instead of a carbon.

By a “first ring atom in R⁶ and R⁷ bound to an imino nitrogen atom” is meant the ring atom in these groups bound to an imino nitrogen shown in (I), for example

the atoms shown in the 1-position in the rings in (II) and (III) are the first ring atoms bound to an imino carbon atom (other groups which may be substituted on the aryl groups are not shown). Ring atoms adjacent to the first ring atoms are shown, for example, in (IV) and (V), where the open valencies to these adjacent atoms are shown by dashed lines (the 2,6-positions in (IV) and the 2,5-positions in (V)).

In one preferred embodiment of (I), R⁶ is

and R⁷ is

wherein:

R⁸ is a halogen, a primary carbon group, a secondary carbon group or a tertiary carbon group; and

R⁹, R¹⁰, R¹¹, R¹⁴, R¹⁵, R¹⁶ and R¹⁷ are each independently hydrogen, hydrocarbyl, substituted hydrocarbyl or a functional group; provided that:

when R⁸ is a halogen or primary carbon group none, one or two of R¹², R¹³ and R¹⁷ are a halogen or a primary carbon group, with the remainder of R¹², R¹³ and R¹⁷ being hydrogen; or

when R⁸ is a secondary carbon group, none or one of R¹², R¹³ and R¹⁷ is a halogen, a primary carbon group or a secondary carbon group, with the remainder of R¹², R¹³ and R¹⁷ being hydrogen; or

when R⁸ is a tertiary carbon group, none or one of R¹², R¹³ and R¹⁷ is tertiary carbon group, with the remainder of R¹², R¹³ and R¹⁷ being hydrogen;

and further provided that any two of R⁸, R⁹, R¹⁰, R¹¹, R¹², R¹³, R¹⁴, R¹⁵, R¹⁶ and R¹⁷ vicinal to one another, taken together may form a ring.

In the above formulas (VI) and (VII), R⁸ corresponds to the second ring atom adjacent to the first ring atom bound to the imino nitrogen, and R¹², R¹³ and R¹⁷ correspond to the other ring atoms adjacent to the first ring atom.

In compounds (I) containing (VI) and (VII), it is particularly preferred that:

if R⁸ is a primary carbon group, R¹³ is a primary carbon group, and R¹² and R¹⁷ are hydrogen; or

if R⁸ is a secondary carbon group, R¹³ is a primary carbon group or a secondary carbon group, more preferably a secondary carbon group, and R¹² and R¹⁷ are hydrogen; or

if R⁸ is a tertiary carbon group (more preferably a trihalo tertiary carbon group such as a trihalomethyl), R¹³ is a tertiary carbon group (more preferably a trihalotertiary group such as a trihalomethyl), and R¹² and R¹⁷ are hydrogen; or

if R⁸ is a halogen, R¹³ is a halogen, and R¹² and R¹⁷ are hydrogen.

In all specific preferred compounds (I) in which (VI) and (VII) appear, it is preferred that R¹, R² and R³ are hydrogen; and/or R⁴ and R⁵ are methyl. It is further preferred that:

R⁹, R¹⁰, R¹¹, R¹², R¹⁴, R¹⁵, R¹⁶ and R¹⁷ are all hydrogen; R¹³ is methyl; and R⁸ is a primary carbon group, more preferably methyl; or

R⁹, R¹⁰, R¹¹, R¹², R¹⁴, R¹⁵, R¹⁶ and R¹⁷ are all hydrogen; R¹³ is ethyl; and R⁸ is a primary carbon group, more preferably ethyl; or

R⁹, R¹⁰, R¹¹, R¹², R¹⁴, R¹⁵, R¹⁶ and R¹⁷ are all hydrogen; R¹³ is isopropyl; and R⁸ is a primary carbon group, more preferably isopropyl; or

R⁹, R¹⁰, R¹¹, R¹², R¹⁴, R¹⁵, R¹⁶ and R¹⁷ are all hydrogen; R¹³ is n-propyl; and R⁸ is a primary carbon group, more preferably n-propyl; or

R⁹, R¹⁰, R¹¹, R¹², R¹⁴, R¹⁵, R¹⁶ and R¹⁷ are all hydrogen; R¹³ is chloro; and R⁸ is a halogen, more preferably chloro; or

R⁹, R¹⁰, R¹¹, R¹², R¹⁴, R¹⁵, R¹⁶ and R¹⁷ are all hydrogen; R¹³ is trihalomethyl, more preferably trifluoromethyl; and R⁸ is a trihalomethyl, more preferably trifluoromethyl.

In another preferred embodiment of (I), R⁶ and R⁷ are, respectively

wherein:

R¹⁸ is a halogen, a primary carbon group, a secondary carbon group or a tertiary carbon group; and

R¹⁹, R²⁰, R²³ and R²⁴ are each independently hydrogen, hydrocarbyl, substituted hydrocarbyl or a functional group; Provided that:

when R¹⁸ is a halogen or primary carbon group none, one or two of R²¹, R²² and R²⁵ are a halogen or a primary carbon group, with the remainder of R²¹, R²² and R²⁵ being hydrogen; or

when R¹⁸ is a secondary carbon group, none or one of R²¹, R²² and R²⁵ is a halogen, a primary carbon group or a secondary carbon group, with the remainder of R²¹, R²² and R²⁵ being hydrogen;

when R¹⁸ is a tertiary carbon group, none or one of R²¹, R²² and R²⁵ is a tertiary carbon group, with the remainder of R²¹, R²² and R²⁵ being hydrogen;

and further provided that any two of R¹⁸, R¹⁹, R²⁰, R²¹, R²², R²³, R²⁴ and R²⁵ vicinal to one another, taken together may form a ring.

In the above formulas (VIII) and (IX), R¹⁸ corresponds to the second ring atom adjacent to the first ring atom bound to the imino nitrogen, and R²¹, R²² and R²⁵ correspond to the other ring atoms adjacent to the first ring atom.

In compounds (I) containing (VIII) and (IX), it is particularly preferred that:

if R¹⁸ is a primary carbon group, R²² is a primary carbon group, and R²¹ and R²⁵ are hydrogen; or

if R¹⁸ is a secondary carbon group, R²² is a primary carbon group or a secondary carbon group, more preferably a secondary carbon group, and R²¹ and R²⁵ are hydrogen; or

if R¹⁸ is a tertiary carbon group (more preferably a trihalo tertiary carbon group such as a trihalomethyl), R²² is a tertiary carbon group (more preferably a trihalotertiary group such as a trihalomethyl), and R²¹ and R²⁵ are hydrogen; or

if R¹⁸ is a halogen, R²² is a halogen, and R²¹ and R²⁵ are hydrogen.

In all specific preferred compounds (I) in which (VIII) and (IX) appear, it is preferred that R¹, R² and R³ are hydrogen; and/or R⁴ and R⁵ are methyl. It is further preferred that:

R¹⁹, R²⁰, R²¹, R²³ and R²⁴ are all hydrogen; R²² is methyl; and R¹⁸ is a primary carbon group, more preferably methyl; or

R¹⁹, R²⁰, R²¹, R²³ and R²⁴ are all hydrogen; R²² is ethyl; and R¹⁸ is a primary carbon group, more preferably ethyl; or

R¹⁹, R²⁰, R²¹, R²³ and R²⁴ are all hydrogen; R²² is isopropyl; and R¹⁸ is a primary carbon group, more preferably isopropyl; or

R¹⁹, R²⁰, R²¹, R²³ and R²⁴ are all hydrogen; R²² is n-propyl; and R¹⁸ is a primary carbon group, more preferably n-propyl; or

R¹⁹, R²⁰, R²¹, R²³ and R²⁴ are all hydrogen; R²² is chloro or bromo, and R¹⁸ is a halogen, more preferably chloro or bromo.

The other type of ethylene olgimerization catalyst is typified by that described in U.S. Pat. No. 5,382,738. Typically these types of catalysts produce (predominantly) a single olefin having a relatively low number of carbon atoms, such as 1-hexene or 1-octene. These types of catalysts may also be used in the present processes to oligomerize ethylene as described in the references concerning these catalysts.

It is preferred that an ethylene oligomerization catalyst system that produces a homologous series of α-olefins be used. It is also preferred that this catalyst system produces a product with a high molar percentage (at least about 80 mole percent preferably at least about 90 mole percent) of olefins of the formula H(CH₂CH₂)_(n)CH═CH₂ (V), wherein n is 1 or more.

The production of the HTAC from hydrogen, aluminum and the α-olefin(s) can be carried out by methods known in the art, see for instance U.S. Pat. Nos. 2,787,626, 3,032,574, 3,207,770 and 3,960,912 and W. Gerhartz, et al., Ed., Ullmann's Encyclopedia of Industrial Chemistry, 5 ^(th) Ed., Vol. A1, VCH Verlagsgesellschaft mbH, Weinheim, 1985, p. 545-549, which is hereby included by reference. The process may be carried out in a single reactor or in a series of reactors as in U.S. Pat. No. 3,960,912. In this patent not all of the ingredients are contacted simultaneously, but all are added to the overall reaction system at some point. This is included within the meaning of contacting the hydrogen, aluminum and olefin(s). Typical reaction conditions in a single reactor are 70 kPa to 20 MPa hydrogen pressure, a temperature of 80° C. to 180° C. for a period of about 1 hour to about 24 hours. The conditions will be interdependent on each other and also on the starting materials used, particularly the α-olefin(s) used. Typically also present in these processes is a trialkylaluminum compound. It is present during the startup of the reaction and may be a trialkylaluminum compound such as triethylaluminum, or it may be a HTAC or mixtures thereof which are meant to be produced in the process. As described in the above mentioned references some of the product HTAC will likely be recycled back to the reactor making the HTAC, and some will be taken off as product.

Preferably the α-olefin(s) from the ethylene oligomerization reaction undergo little or no purification before being put into the process to make the HTAC. If a mixture of α-olefins are produced they are preferably not separated. The ethylene oligomerization catalyst may be deactivated or not (if present ft may be deactivated by the usually higher temperatures of the HTAC forming process). A solvent may be used in the ethylene oligomerization reaction, and preferably it does not contain active hydrogen compounds such as water, alcohols or carboxylic acids. If the solvent does not contain active hydrogen compounds it does not need to be separated before the reactions to form the HTAC. Preferred solvent in the oligomerization reaction, if any, are nonolefinic hydrocarbons such as toluene, xylene, octane, cyclohexane, and the like. The composition of the HTAC(s) produced will depend on the composition of the α-olefin (mixture) added to the HTAC forming reaction.

Reaction of the HTAC(s) with oxygen or other oxidizing agent to form higher trialkoxyaluminum compounds can be carried out as known in the art, see for instance . Elvers, et al., Ed., Ullmann's Encyclopedia of Industrial Chemistry, 5^(th) Ed., Vol. A28, VCH Verlagsgesellschaft mbH, Weinheim, 1996, p. 505-508 and references therein, and U.S. Pat. No. 5,278,330 which is hereby included by reference. Likewise, the hydrolysis of the higher trialkoxyaluminum compound to form α-alcohols may be carried out by methods known in the literature, see for instance Elvers, et al., Ed., Ullmann's Encyclopedia of Industrial Chemistry, 5^(th) Ed., Vol. A28, VCH Verlagsgesellschaft mbH, Weinheim, 1996, p. 505-508 and references therein, and U.S. Pat. No. 5,278,330. These methods for oxidation and hydrolysis to form α-alcohols are known in the art.

The present process form making the HTAC(s) and/or α-alcohols result in less handling of pyrophoric alkylaluminum compounds at high temperatures and/or pressure, thereby making the process safer and/or lowering operating cost, and/or lowering investment need for the plant, when compared to the conventional methods of manufacturing these types of compounds. Assuming a mixture of homologous α-olefins is used to make the HTAC, the product mixture resulting, for example, from making α-alcohols may be similar to that obtained with current manufacturing methods. 

What is claimed is:
 1. A process for the manufacture of higher trialkylaluminum compounds, comprising, forming an α-olefin or mixture of α-olefins by oligomerization of ethylene using a transition metal containing oligomerization catalyst system, then contacting said α-olefin or said mixture of α-olefins with aluminum metal, hydrogen and a trialkylaluminum compound at a sufficient temperature and pressure, for a sufficient amount of time, to form a higher trialkylaluminum compound.
 2. A process for the manufacture of α-alcohols, comprising: (1) forming an α-olefin or mixture of α-olefins by oligomerization of ethylene using a transition metal containing oligomerization catalyst system; (2) then contacting said α-olefin or said mixture of α-olefins with aluminum metal, hydrogen and a trialkylaluminum compound at a sufficient temperature and pressure, for a sufficient amount of time, to form a higher trialkylaluminum compound or a mixture thereof; (3) contacting said higher trialkylaluminum compound or a mixture thereof with oxygen or other suitable oxidizing agent to form a higher trialkoxyaluminum compound or a mixture thereof; and (4) hydrolyzing said higher trialkoxyaluminum compound or a mixture thereof to form an α-alcohol or a mixture thereof.
 3. The process as recited in claim 1 or 2 wherein said mixture of olefins is used and is a homologous series of α-olefins.
 4. The process as recited in claim 1 or 2 wherein said homologous series of α-olefins is produced in an oligomerization reaction which has a Schulz-Flory constant of about 0.6 to about 0.8.
 5. The process as recited in claim 1, 2, 3 or 4 wherein said transition metal containing oligomerization catalyst system comprises an iron complex of a diimine of a 2,6-diacylpyridine or a 2,6-pyridinedicarboxaldehyde.
 6. The process as recited in claim 5 wherein said iron complex is a compound of the formula

wherein: R¹, R² and R³ are each independently hydrogen, hydrocarbyl, substituted hydrocarbyl or an inert functional group, provided that any two of R¹, R² and R³ vicinal to one another taken together may form a ring; R⁴ and R⁵ are each independently hydrogen, hydrocarbyl, substituted hydrocarbyl or an inert functional group; R⁶ and R⁷ are each independently a substituted aryl having a first ring atom bound to the imino nitrogen, provided that: in R⁶, a second ring atom adjacent to said first ring atom is bound to a halogen, a primary carbon group, a secondary carbon group or a tertiary carbon group; and further provided that in R⁶, when said second ring atom is bound to a halogen or a primary carbon group, none, one or two of the other ring atoms in R⁶ and R⁷ adjacent to said first ring atom are bound to a halogen or a primary carbon group, with the remainder of the ring atoms adjacent to said first ring atom being bound to a hydrogen atom; or in R⁶, when said second ring atom is bound to a secondary carbon group, none, one or two of the other ring atoms in R⁶ and R⁷ adjacent to said first ring atom are bound to a halogen, a primary carbon group or a secondary carbon group, with the remainder of the ring atoms adjacent to said first ring atom being bound to a hydrogen atom; or in R⁶, when said second ring atom is bound to a tertiary carbon group, none or one of the other ring atoms in R⁶ and R⁷ adjacent to said first ring atom are bound to a tertiary carbon group, with the remainder of the ring atoms adjacent to said first ring atom being bound to a hydrogen atom.
 7. The process as recited in claim 1 or 2 wherein a single α-olefin is used. 